| 원료: | 강옥과 멀라이트 | 맞춤형: | 예 |
|---|---|---|---|
| 설치방법: | 진동 캐스팅 | 파손 강도: | 1100℃×3h에서 ≥6Mpa |
| 용법: | 퍼니스 라이너, 라이닝 주조 작업 | 굴곡강도: | 1d ≥6.0MPa |
| 굴절성: | 1700°C 이상 | 제품: | 산성 내성 캐스트 가능 |
| 작동 온도: | 1800 ℃ | 압축력강도: | ≥ 50MPa(경화 3일 후) |
| 어플리케이션: | 코크 오븐 | 적용온도: | 최대 1800 ° C |
| 유형: | 제조 | 만들어집니다: | HENAN |
| 알루미나 콘텐츠: | 50% | ||
| 강조하다: | high temperature refractory gunning mix,alumina silicate spray coatings,induction furnace refractory castable |
||
Rongsheng Refractory Gunning Materials High Refractoriness Alumina Silicate Spray Coatings Induction Furnace Refractory Gunning Mix
Refractory Gunning Mix:
Gunning mix is composed of refractory aggregate, refractory powder, water, binder, mineralizer, plasticizer, and firing aid. It is a fire-resistant mixture constructed by spraying method.The materials of gunning mix include silicon aluminum, magnesium, corundum, and phosphate. It is also divided into lightweight,medium heavy weight and heavy weight gunning mix.
Light weight gunning mix is used for thermal insulation and insulation lining, medium heavy weight can be used as both thermal insulation and working lining for mediuContact Usm and low temperature furnaces, heavy weight gunning mix is mainly used as working lining.
Features and Advantages of Refractory Gunning Mix
refractory gunning mix has the characteristics of high adhesive rate,less resilience,high strength and easy gunning etc.scour resistance,impact resistance,erosion resistance.anti-scouring, wear resistance and excellent performances.
Application of Refractory Gunning Mix
Steel Industry,Energy Industry,Building Materials.It serves as a protective layer on the inner surface of blast furnace and hot blast furnace shells, as well as a working lining for blast furnace heads, coal gas outlet pipe, and dust collectors.
Refractory Material Gunning Mix Technique Data
| Item | Specification | |||
| LGP0.8 | LGP1.0 | LGP1.3 | ||
| Al2O3 % | ≥30 | ≥35 | ≥40 | |
| Bulk Density,g/cm3 110℃×24h | ≤0.8 | ≤1.0 | ≤1.3 | |
| CCS, MPa | 110℃×24h | ≥4 | ≥5 | ≥7 |
| Test Temperature, ×3h | ≥3 800℃ | ≥4 1000℃ | ≥5 1200℃ | |
| PLC, % Test Temperature, ×3h |
±0.8 800℃ |
±0.8 1000℃ |
±0.8 1200℃ |
|
| Thermal Conductivity, W/(m·K) 350℃±25℃ | ≤0.21 | ≤0.25 | ≤0.35 | |
| Test Temperature, ℃ | 800 | 1000 | 1200 | |
| Item | Specification | |||
| LGP1.5 | LGP1.8 | LGP1.8T | ||
| Al2O3 % | ≥42 | ≥45 | ≥55 | |
| Bulk Density,g/cm3 110℃×24h | ≤1.5 | ≤1.8 | ≤1.8 | |
| CCS, MPa | 100℃×24h | ≥12 | ≥15 | ≥12 |
| Test Temperature, ×3h | ≥10 1300℃ | ≥13 1300℃ | ≥10 1400℃ | |
| PLC, % Test Temperature×3h |
±0.8 1300℃ |
±0.8 1300℃ |
±1.0 1400℃ |
|
| Thermal Conductivity, W/(m·K) 350℃±25℃ | ≤0.4 | ≤0.7 | ≤0.75 | |
| Max Working Temperature, ℃ | 1300 | 1300 | 1500 |
|